TIODIZE has developed a full range of FIBER/LITE fasteners
and fastening devices made of state of the art composites.
These products maintain high tensile, shear and fatigue
strength at temperatures to 700°F.
FIBER/LITE can be processed into a variety of signature
free, non-corrosive shapes and sizes equivalent in strength
to aluminum at two thirds the weight.
These components are manufactured by compression, matched-die
molding and show excellent dimensional stability through
repeated heating/cooling cycles and exposure to water
or water vapor, solvents and oils.
|
|
Contact the TIODIZE Engineering Department
to review your drawings and specifications.
We look forward to working with you to develop composite
parts that meet your requirements. |
|
|
|
| |
FIBER/LITE MATERIAL
PROPERTIES
|
| |
ECFG |
TDF-3 |
PLFC |
| Density |
1.81 - 1.85 g/CM3 |
1. 5 g/cm3 |
1.5 - 1.55 g/cm3 |
| |
.065 - .067 lb/in3 |
|
|
| Flexural Strength |
58,000 psi |
39,800 psi @ 600°F |
|
| Flexural Modulus |
2.6 x 106 psi |
2.2 x 106 psi @ 600°F |
|
| Tensile Strength @ 75°F |
33,000 psi |
30,000 psi @ 600°F |
50,000 psi |
| with threads @ -320°F |
22,000 psi |
|
|
| Tensile Modulus |
3.4 x 106 psi |
12 x 106 psi @ 600°F |
|
| Tensile Elongation |
1% |
Less than 1% |
1% |
| Compressive Strength |
75°F
|
33,000 psi |
30,000 psi |
33,000 psi |
| |
300°F |
10,400 psi |
|
|
| |
400°F |
6,100 psi |
|
|
| |
600°F |
|
40,000 psi |
|
| Double Lap Shear Strength |
30,000 psi |
24,000 psi |
|
| Single Shear |
|
31,000psi |
50,000 psi |
| Heat Distortion Temperature @ 265 psi |
+575°F |
|
|
| Continuous Use Temperature (1000 hours) |
400°F |
700°F |
500°F |
| Coefficient of Thermal Expansion |
7 x 10-6 in/in/°F |
<1 x 10-6 in/in/°F |
<1 x 10-6 in/in/°F * |
| Water Absorption (24 hrs. @ 23 C) |
0.08% |
|
0.06% |
| (D.I. H2O Soak) (7 days @ 23 C) |
0.28% |
1.1% |
0.2% |
| Poisson's Ratio |
0.30 |
|
|
| Thermal Conductivity |
6.8 X 10-4 |
2-3 x 10-2 |
2-3 x 10-2 |
| |
cal/sec-cm2 °C/cm |
cal/sec-cm2 °C/cm |
cal/sec-cm2 °C/cm |
Thread Load Carrying Capacity
1/4" Thick Panel w/1/4" Threaded
Hole w/Steel Bolt (Coarse Threads) |
2,000 lbs. |
|
|
| Volume Resistivity |
> 3 x 1014 ohm-cm |
Conductive |
Conductive |
| Dielectric Strength |
500 v/mil |
Conductive |
Conductive |
| Dielectric Constant (100 Hz) |
4.3 |
Conductive |
Conductive |
| Dissipation Factor (100 Hz) |
0.007 |
|
|
|
* in direction of fiber
|
|